상수도용 대구경 녹 발생 강관 내부의 보수 및 성능 유지를 위한EVA 시트와 부틸고무를 합지한 자착식 방수방식 시트의 부착성능 평가

This study discusses the applicability of environmental friendly EVA based butyl rubber self-adhesive waterproof sheet designed to prevent corrosion of large scale pipes used in the water treatment facilities during th water treatment process. The experiments conducted tested the waterproofing sheet‘s adhesion strength on the steel surface of the pipes and checked for whether the material has the proper response properties against the various environmental conditions. In addition, it the sheet adhered to the steel pipe was to see if the adhesion hold against the water pressure due to the ingress of inflow water. Finally, the waterproofing sheet’s adhesion strength was tested on a rusted steel surface to confirm whether the material has the necessary properties to secure stable adhesion strength and prevent corrosion of steel pipes at the same time during the process of installation or maintenance. As a result, the self-adhesive waterproof sheets showed that all attachments in the untreated, long term pressuring, immersion in chemical substance (hydrochloric acid, hypochlorous acid, sodium hydroxide), low temperature (-20°C) conditions showed a adhesion performance of higher than 1.5N/mm, which is the performance standard of KS F 4934. Also, in the testing to check for the adhesion property against inverse water pressure, it was observed that the adhesion failure did not occur even up to 3.0N/mm2 pressure. Also, in the process of assessing the adhesion performance on rusted steel surface, specimens after 12 hours of corrosion treatment was shown to have 2.1N/mm, and specimens after 168 hours of corrosion treatment was shown to have 2.0N/mm adhesion strength performance.