하이드로퀴논 환원제를 사용한 은코팅 구리 플레이크의 제조에서 공정 변수의 영향

In the process for preparing Ag-coated Cu flakes by electroless silver plating using hydroquinone reducing agent, Ag coating qualities were compared by changing various process parameters such as type of pretreatment solution, plating temperature, pH of plating solution, type and injection rate of plating solution, and pulp density. Effective pretreatment solution for removing the oxide layer on a Cu flake was preferentially suggested. The conditions of low plating temperature, pH value of 4.34, slow injection rate of Ag plating solution, elimination of deionized water in the Ag plating solution, and high pulp density significantly suppressed the formation of separated tiny Ag particles, and thus the surface coverage of Ag coating on Cu flakes was enhanced.