Reduction characteristics of CuFe₂O₄ and Fe₃O₄ by methane; CuFe₂O₄ as an oxidant for two-step thermochemical methane reforming

The reduction characteristics of CuFe₂O₄ and Fe₃O₄ by methane at 600-900 °C were determined in a thermogravimetric analyzer for the purpose of using CuFe₂O₄ as an oxidant of two-step thermochemical methane reforming. It was found that the addition of Cu to Fe₃O₄ largely affected the reduction kinetics and carbon formation in methane reduction. In the case of CuFe₂O₄, the reduction kinetics was found to be faster than that of Fe₃O₄. Furthermore, carbon deposition and carbide formation from methane decomposition were effectively inhibited. In case of Fe₃O₄, Fe metal formed from Fe₃O₄ decomposed methane catalytically, that lead to the formation of graphite and Fe₃C phases. It is deduced that Cu in CuFe₂O₄ enhanced reduction kinetics, decreased reduction temperature and prevented carbide and graphite formation. Additionally, methane conversion and CO selectivity in the syngas production step with CuFe₂O₄ were in the range of 33.5-55.6% and 54.9-59.6%, respectively.