Strongly enhanced flux pining of GdBCO coated conductors with BaSnO ₃ nanorods by pulsed laser deposition

We report the effects of BSO addition on the crystallinity, texture, and the field dependency of critical current density (J_c) of GdBCO coated conductors (CCs) prepared by pulsed laser deposition (PLD). Undoped and BSO-doped GdBCO films showed only c-axis oriented growth, and the incorporated BSO nanorods exhibited epitaxial relationship with the GdBCO matrix. In comparison with undoped film, BSO-doped GdBCO film exhibited greatly enhanced J_c and higher pinning force densities in the entire field region of 0-5 T (H//c) at 77 and 65 K. The BSO-doped GdBCO film showed the maximum pinning force densities (F_p) of 6.5 GN/m³ (77 K, H//c) and 32.5 GN/m³ (65 K, H//c), ∼2.8 times higher than those of the undoped sample. Cross-sectional TEM analyses exhibited nano-structured BSO nanorods roughly aligned along the c-axis of the GdBCO film, which are believed effective flux pinning centers responsible for strongly improved critical current densities in magnetic fields.